This series products adopt high quality raw material, adding American Dupont Teflon high temperature resistance new materials, high temperature processing, have a wear-resistant, high temperature resistance, good printing effect, etc., good elasticity, flexibility, long service life , even for irregular surface of the fine pattern can also ensure a clear print results. Ink stick completely, easily de-inking transfer, residual ink easy to remove. Specification is complete, easy to user specific requirements can be special. 
 Product Use: 
 Mainly used in plastic toys, electroplating products, electronic toys, trademarks and irregular pattern printing. Pad printing a pattern on the plate is to head through the plastic carrier to do, then transfer the pattern on the plate in the toy products. 



 Pad printing silicone product manual 
 First, the first mold cleaned with detergent, then dry the mold in the water or dry, and coated with a layer of release agent. 
 Second, the silicone pad, silicone oil in the normal ratio is determined according to customer requirements, if the customer requires the printing pattern area, required soft head, the more increase in silicone oil. Rather, it is the first hardness of rubber, silicone oil is not added or less to add, the hardness of general pad printing rubber head to 15A ~-25A ° to the right, if you add excessive silicone oil, plastic head is too soft, the number of printing was limited, even the best quality silicone will be destroyed its molecular weight silicone oil, and produce wear-resistant, non-solvent, and aging. 
 Third, the introduction of the normal ratio is as follows: 100 grams of silica gel by adding 30 g silicone oil to meet the printing and design alloy Trolley small, relatively small contact area of ??the product. Contact surface, if any, pressure or head to be soft, silicone and silicone oil ratio can be 100:30,100:50 range, but note that the greater the amount of silicone oil added, the more soft plastic head, printing the number of times, wear resistance and solvent resistance are reduced and the reduction in the number of printing products will be reduced, resulting in rising costs, raw material waste. 
 Fourth, add the amount of curing agent and the silica gel ratio of chemical reaction as follows: Take 100 g silica gel, silicone oil, 50 grams, and then mixing until fully stirred silicone oil after silica gel, then the total weight of silica and silicone oil add 2% -3% curing agent, then stir for 2-3 minutes, you can be taking the time. Taking the time to be not more than 10 minutes, taking the time too long, fast curing gel, it will affect the quality of glue down. 